Remarkable improvement of damping capacity in FeMn-based alloys by a long annealing
-
- Wei He
- School of Mechanical Engineering, Sichuan University, Chengdu, People's Republic of China
-
- Qiang Luo
- School of Mechanical Engineering, Sichuan University, Chengdu, People's Republic of China
-
- Huabei Peng
- School of Mechanical Engineering, Sichuan University, Chengdu, People's Republic of China
-
- Yuhua Wen
- School of Mechanical Engineering, Sichuan University, Chengdu, People's Republic of China
Abstract
<jats:p> Effects of a long annealing up to 10 h were investigated on damping capacity and phase evolutions in FeMn-based alloys. The damping capacity in the Fe17.5Mn alloy rose with the annealing time. A highest damping capacity was obtained in the Fe16.5Mn10.5Cr alloy after 2 h annealing. The highest damping capacity was comparable in Fe17.5Mn and Fe16.5Mn10.5Cr alloys. A positive relationship between the damping capacity and the stacking faults existed in both the Fe17.5Mn and Fe16.5Mn10.5Cr alloys annealed for above 2 h. To reduce the amount of α′-martensites was favourable to the further improvement of damping capacity. The α′-martensites clustered locally in the Fe17.5Mn alloy, but they distributed inside the ϵ-martensite bands in the Fe16.5Mn10.5Cr alloy. </jats:p>
Journal
-
- Materials Science and Technology
-
Materials Science and Technology 36 (12), 1329-1336, 2020-08
SAGE Publications