Effect of Minor Addition of Oxygen on Bulk Metallic Glass Formation of Binary Cu–Zr Alloys via Containerless Processing

DOI Web Site Web Site Web Site 参考文献28件
  • Akitoshi Mizuno
    Department of General Education National Institute of Technology, Hakodate College Hokkaido 042-8501 Japan
  • Takeshi Harada
    Department of Physics Gakushuin University Tokyo 171-8588 Japan
  • Masahito Watanabe
    Department of Physics Gakushuin University Tokyo 171-8588 Japan

この論文をさがす

説明

<jats:sec><jats:label/><jats:p>The effect of oxygen content on the glass‐forming ability of binary Cu–Zr alloys is investigated by the in situ observation of the cooling process during the containerless solidification using an aerodynamic levitation technique. The oxygen content of ≈0.72 at% induces the crystallization of undercooled liquid Cu<jats:sub>47</jats:sub>Zr<jats:sub>53</jats:sub> alloy, whereas that of ≈0.33 at% enhances the glass‐forming ability and leads to the formation of bulk metallic glass when compared with the alloy containing ≈0.20 at% of oxygen. The differential thermal analysis of the bulk metallic glass samples shows the extension of the undercooled liquid region with an increase in the oxygen content from 0.20 to 0.33 at% in the Cu<jats:sub>47</jats:sub>Zr<jats:sub>53</jats:sub> alloy. Time‐resolved synchrotron X‐ray diffraction experiments reveal structure evolution of the Cu<jats:sub>47</jats:sub>Zr<jats:sub>53</jats:sub> alloy from the undercooled liquid to glass or crystal. The effect of oxygen on the glass‐forming ability is qualitatively described in terms of reducing the critical cooling rate of the alloy.</jats:p></jats:sec>

収録刊行物

参考文献 (28)*注記

もっと見る

関連プロジェクト

もっと見る

問題の指摘

ページトップへ