Improved Oxygen Redox Activity by High-Valent Fe and Co<sup>3+</sup> Sites in the Perovskite LaNi<sub>1–<i>x</i></sub>Fe<sub>0.5<i>x</i></sub>Co<sub>0.5<i>x</i></sub>O<sub>3</sub>
-
- Anjaiah Sheelam
- Institute of Physics, Academia Sinica, Nangang District, Taipei 11529, Taiwan
-
- Sakthipriya Balu
- Department of Mechanical Engineering, National Taiwan University of Science and Technology, No. 43, Section 4, Keelung Road, Taipei 10607, Taiwan
-
- Adil Muneeb
- Department of Mechanical Engineering, National Taiwan University of Science and Technology, No. 43, Section 4, Keelung Road, Taipei 10607, Taiwan
-
- Khasim Saheb Bayikadi
- Institute of Physics, Academia Sinica, Nangang District, Taipei 11529, Taiwan
-
- Dhenadhayalan Namasivayam
- Institute of Atomic and Molecular Sciences, No. 1, Section 4, Da’an District, Taipei 10617, Taiwan
-
- Erakulan E. Siddharthan
- SRM University, No. 5, Annamaya Circle, Tirupati, Andhra Pradesh 522240, India
-
- Arif I. Inamdar
- Institute of Chemistry, Academia Sinica, Nangang District, Taipei 11529, Taiwan
-
- Ranjit Thapa
- SRM University, No. 5, Annamaya Circle, Tirupati, Andhra Pradesh 522240, India
-
- Ming-Hsi Chiang
- Institute of Chemistry, Academia Sinica, Nangang District, Taipei 11529, Taiwan
-
- Song-Jeng Isaac Huang
- Department of Mechanical Engineering, National Taiwan University of Science and Technology, No. 43, Section 4, Keelung Road, Taipei 10607, Taiwan
-
- Raman Sankar
- Institute of Physics, Academia Sinica, Nangang District, Taipei 11529, Taiwan
収録刊行物
-
- ACS Applied Energy Materials
-
ACS Applied Energy Materials 5 (1), 343-354, 2022-01-07
American Chemical Society (ACS)