Fabrication of Mullite and Mullite‐Matrix Composites by Transient Viscous Sintering of Composite Powders

DOI Web Site Web Site 被引用文献1件

書誌事項

公開日
1991-10
権利情報
  • http://onlinelibrary.wiley.com/termsAndConditions#vor
DOI
  • 10.1111/j.1151-2916.1991.tb06780.x
公開者
Wiley

この論文をさがす

説明

<jats:p>Mullite was fabricated by a process referred to as transient viscous sintering (TVS). Composite particles which consisted of inner cores of α‐alumina and outer coatings of amorphous silica were used. Powder compacts prepared with these particles were viscously sintered to almost full density at relatively low temperatures (∼1300°C). Compacts were subsequently converted to dense, fine‐grained mullite at higher temperatures (∼1500°C) by reaction between the alumina and silica. The TVS process was also used to fabricate mullite/zirconia/alumina, mullite/silicon carbide particle, and mullite/silicon carbide whisker composites. Densification was enhanced compared with other recent studies of sintering of mullite‐based composites. This was attributed to three factors: viscous flow of the amorphous silica coating on the particles, avoidance of mullite formation until higher temperatures, and increased threshold concentration for the development of percolation networks.</jats:p>

収録刊行物

被引用文献 (1)*注記

もっと見る

問題の指摘

ページトップへ