Pb1 − xSnxTe crystals were grown by the directional solidification method under microgravity in the SL-J/FMPT mission on board the space shuttle “Endeavor”. A cylindrical crystal, 15 mm in diameter and 58 mm in length, was obtained. A constant SnTe mole fraction of about 0.16 (i.e., a constant PbSn ratio) was achieved along the growth axis to a distance of about 10 mm, and the etch pit density was about one-tenth that of a terrestrially grown crystal. The space-grown crystal had also improved electrical properties. In addition, about 25 spherical crystals, ranging from 0.5 to 11 mm in diameter, were unintentionally formed on the graphite spring.
収録刊行物
-
- Journal of Crystal Growth
-
Journal of Crystal Growth 147 (1-2), 91-98, 1995-01