The oxidation behaviour of silicon nitride composed of Si3N4, Y2O3, Al2O3, AlN and TiO2 was investigated in dry and wet air at 1100–1400 °C. The oxidation rates were confirmed to obey the parabolic law. An activation energy of 255 kJ mol−1 was calculated from the Arrhenius plots of the results of oxidation in an air flow. In still air the oxidation rate was larger than that in an air flow, but the oxidation rate in flowing air was not affected by the air flow rate. α-cristobalite and Y2O3·2SiO2 were formed in oxidized surface layers. These crystal phases increased with increasing oxidation temperature. In particular, a higher content of α-cristobalite was obtained in still air oxidation. The existence of water vapour in flowing air greatly promoted the oxidation.

収録刊行物

被引用文献 (5)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ