Effect of “additional shear strain layer” on tensile strength and microstructure of fine drawn wire

DOI Web Site Web Site 被引用文献3件

この論文をさがす

説明

Abstract Fine wires of the order of 0.1 mm in diameter have become popular for mechanical and electrical applications. In the drawing process, a large shear deformation zone with a hardened layer, referred to as the “additional shear strain layer”, is generated beneath the surface layer of the wire. This study clarified that the depth of this additional shear strain layer was about 0.04 mm for various diameter fine wires. As the diameter decreases, the area ratio of additional shear layer increases. Hence, the additional shear strain layer is a factor for the improvement in high strength and ductility of the wires. In order to discuss the cause of the increase in the surface layer's tensile strength, the crystal orientation was measured via the electron back-scatter diffraction (EBSD) method. It was ascertained that the crystal of surface layer was subdivided more easily than the center layer, and therefore the tensile strength of surface layer increased.

収録刊行物

被引用文献 (3)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ