Strength and Fracture Toughness of Isostatically Hot‐Pressed Composites of Al <sub>2</sub> O <sub>3</sub> and Y <sub>2</sub> O <sub>3</sub> ‐Partially‐Stabilized ZrO <sub>2</sub>

DOI Web Site Web Site 被引用文献14件

書誌事項

公開日
1985-01
権利情報
  • http://onlinelibrary.wiley.com/termsAndConditions#vor
DOI
  • 10.1111/j.1151-2916.1985.tb15251.x
公開者
Wiley

この論文をさがす

説明

<jats:p> Composites of Al <jats:sub>2</jats:sub> O <jats:sub>3</jats:sub> and Y <jats:sub>2</jats:sub> O <jats:sub>3</jats:sub> partially‐stabilized ZrO <jats:sub>2</jats:sub> were isostatically hot‐pressed using submicrometer powders as the starting material. The addition of Al <jats:sub>2</jats:sub> O <jats:sub>3</jats:sub> resulted in a large increase in bending strength. The average bending strength for a composite containing 20 wt% Al <jats:sub>2</jats:sub> O <jats:sub>3</jats:sub> was 2400 MPa, and its fracture toughness was 17 MN·w <jats:sup>−3/2</jats:sup> </jats:p>