Effect of incorporation of graphene oxide and graphene nanoplatelets on mechanical and gas permeability properties of poly(lactic acid) films

DOI Web Site Web Site 被引用文献1件

書誌事項

公開日
2012-06-21
権利情報
  • http://onlinelibrary.wiley.com/termsAndConditions#vor
DOI
  • 10.1002/pi.4290
公開者
Wiley

この論文をさがす

説明

<jats:title>Abstract</jats:title><jats:p><jats:bold>Nanocomposite thin films of poly(lactic acid) (PLA) were produced incorporating small amounts (0.2 to 1 wt%) of graphene oxide (GO) and graphene nanoplatelets (GNP). The films were prepared by solvent‐casting. Mechanical properties were evaluated for plasticized (by residual solvent) and unplasticized films. Plasticized nanocomposite films presented yield strength and Young's modulus about 100% higher than those of pristine PLA. For unplasticized films improvements in tensile strength and Young's modulus were about 15 and 85%, respectively. For both film types, a maximum in mechanical performance was identified for about 0.4 wt% loadings of the two filler materials tested. Permeabilities towards oxygen and nitrogen decreased, respectively, three‐ and fourfold in films loaded with both GO or GNP. The glass transition temperature showed maximum increases, in relation to unloaded PLA films, of 5 °C for 0.4 wt% GO and 7 °C for 0.4 wt% GNP, coinciding with the observed maxima in mechanical properties. Copyright © 2012 Society of Chemical Industry</jats:bold></jats:p>

収録刊行物

被引用文献 (1)*注記

もっと見る

問題の指摘

ページトップへ