Tuning the Relative Concentration Ratio of Bulk Defects to Surface Defects in TiO<sub>2</sub> Nanocrystals Leads to High Photocatalytic Efficiency
-
- Ming Kong
- State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, 122 Luoshi Road, Wuhan 430070, P.R. China
-
- Yuanzhi Li
- State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, 122 Luoshi Road, Wuhan 430070, P.R. China
-
- Xiong Chen
- State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, 122 Luoshi Road, Wuhan 430070, P.R. China
-
- Tingting Tian
- State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, 122 Luoshi Road, Wuhan 430070, P.R. China
-
- Pengfei Fang
- Department of Physics, Wuhan University, Luojia Hill, Wuhan 430072, P.R. China
-
- Feng Zheng
- Department of Physics, Wuhan University, Luojia Hill, Wuhan 430072, P.R. China
-
- Xiujian Zhao
- State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, 122 Luoshi Road, Wuhan 430070, P.R. China
書誌事項
- 公開日
- 2011-09-22
- DOI
-
- 10.1021/ja207826q
- 公開者
- American Chemical Society (ACS)
この論文をさがす
収録刊行物
-
- Journal of the American Chemical Society
-
Journal of the American Chemical Society 133 (41), 16414-16417, 2011-09-22
American Chemical Society (ACS)