Direct Measurement of Fracture Energies of Brittle Heterogeneous Materials

DOI Web Site Web Site 被引用文献5件

書誌事項

公開日
1965-11
権利情報
  • http://onlinelibrary.wiley.com/termsAndConditions#vor
DOI
  • 10.1111/j.1151-2916.1965.tb14677.x
公開者
Wiley

この論文をさがす

説明

<jats:p> A noncatastrophic fracture was shown to exist in the three‐point bending test with a “hard‐beam” machine when an artificially cracked or notched specimen was used. In this mode of fracture the energy produced by external work was transformed completely into the effective surface energy (fracture energy) of the specimen. The energy was measured from the load‐time curve for the test. The fracture energies obtained by this method for plate glass were in the range 3 to 6 × 10 <jats:sup>3</jats:sup> ergs cm <jats:sup>−2</jats:sup> , in good agreement with results obtained by other methods. The effective fracture energies of firebrick were about one order of magnitude larger than those of glass. </jats:p>