硫酸水素アンモニウム融解による難溶性タングステン化合物の迅速分解と分析への応用

DOI 機関リポジトリ NDLデジタルコレクション Web Site Web Site 被引用文献2件 参考文献13件

書誌事項

タイトル別名
  • Rapid decomposition and analysis of refractory tungsten compounds by fusion with ammonium hydrogen sulfate.
  • リュウサン スイソ アンモニウム ユウカイ ニヨル ナンヨウセイ タングステン

この論文をさがす

抄録

A simple and rapid method for the decomposition of refractory tungsten compounds has been proposed. The tungsten samples (WO3, WS2, WC, alloys and ores) were de-composed by fusion with ammonium hydrogen sulfate, which was found to be a suitably powerful flux for dissolving various refractory tungsten compounds. An accurately weighed sample (ca. 4050 mg) was placed in a dry Pyrex glass test-tube (16 mm o.d., 180 mm length). Ammonium hydrogen sulfate (ca. 2 g) was added to the tube and mixed with the sample by agitating of the tube. The bottom of the test tube was gently heated with a swirling motion over a small gas flame of a Bunsen burner with a fish-tail at a temperature of ca. 350450°C. Heating was continued until a clean, translucent yellow melt was formed. The cooled melt was dissolved in a 10% (w/v) ammonium tartrate solution. Tungsten(VI) oxide and sulfide were dissolved by heating for about 4 min, for carbide it was about 8 min. Finally, the concentration of the tungsten in the, resulting solution was determined by atomic-absorption spectrometry using a dinitrogen oxide-acetylene flame. This method was applied successfully to various hard metals and ores (scheelite). The tungsten, cobalt and iron in the samples were determined.

収録刊行物

  • 分析化学

    分析化学 46 (2), 101-105, 1997

    公益社団法人 日本分析化学会

被引用文献 (2)*注記

もっと見る

参考文献 (13)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ