二酸化マンガン共沈分離/メタル炉原子吸光法による鉄,銅及びニッケル中のヒ素の定量

書誌事項

タイトル別名
  • Determination of arsenic in iron, copper and nickel by metal furnace AAS after coprecipitation with manganese dioxide.
  • 2サンカ マンガン キョウチン ブンリ メタルロ ゲンシ キュウコウホウ ニ

この論文をさがす

抄録

Metal furnace AAS has been used to determine arsenic (As) in iron, copper and nickel. The proposed analytical procedure is as follows : sample (0.12.0 g) was dissolved in 2030 ml of HNO3 (1+1). The pH except for the case of Fe samples was adjusted to pH 1.02.0 with aqueous ammonia. Arsenic (As) was coprecipitated with manganese dioxide by adding KMnO4 and Mn2+. If more than 50 μg of Sn was contained in Cu or Ni, 0.2 g of Fe had to be added in order to coprecipitate As from HNO3 solution, because Sn(OH)4 was formed in the solution (pH 1.02.0) and it interfere with dissolving the precipitate. The precipitate was dissolved in a mixture of HNO3-H2O2 to which 5 mg of Ca was added and the solution diluted to 50 ml with water. Twenty microliters of this solution was injected into a tungsten boat, and dried at 180°C, for 30 s, ashed at 1500°C for 20 s by ramp mode, and then atomized at 2300°C for 2 s. The absorbance of As was interfered with the matrices of sample solutions, but addition of 100 μg/ml alkaline-earth metals (Ca, Mg and Ba) proved to eliminate these interferences. The same calibration curve prepared with standard solutions could be used for any samples. Fairly accurate results were obtained by this method for NIST, BAS and BAM standards.

収録刊行物

  • 分析化学

    分析化学 40 (1), 33-37, 1991

    公益社団法人 日本分析化学会

被引用文献 (8)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ