Control of Spatial Periodicities of Dewetting Structures of Oleo-Liquid Films
-
- KURODA Akihiro
- Department of Applied Chemistry, Faculty of Science and Technology, Keio University Cosmetechno Co., Ltd., Yokohama Office
-
- TAKESHIGE Hikari
- Department of Applied Chemistry, Faculty of Science and Technology, Keio University
-
- ASAKURA Kouichi
- Department of Applied Chemistry, Faculty of Science and Technology, Keio University
この論文をさがす
説明
Thin liquid films containing octyl p-methoxycinnamate (OPMC) and octylsilyl titanium dioxide particle having average diameter of 35 nm (OSI-TIO2-35) were prepared on glass plates. The content of OSI-TIO2-35 to OPMC was varied from 8:2 to 2:8 and the film thickness was from 0.050 to 0.200 mg/cm2. The liquid films underwent dewetting when immersed into water at 35°C for 10 min to form long cylindrical ridged patterns or droplet patterns. The dewetting patterns were confirmed to be spatially periodic by two-dimensional fast Fourier transform indicating that the first stage of the dewetting was spinodal dewetting, i.e., formation of holes by amplification of surface fluctuation followed by growth and coalescence of holes. Both thickness and content of the films influenced on the dewetting pattern formation. Dewetting occurred more easily as decreasing the film thickness. Droplet patterns tended to be formed as increasing the content of OPMC. Characteristic length of the dewetting patterns decreased as increasing the content of OSI-TIO2-35 and decreasing the film thickness. Wave vector of fluctuation having the highest growth rate is influenced by film thickness and interfacial tension. Interfacial tension and viscosity of the liquid film are easily adjusted by changing the ratio of OPMC to OSI-TIO2-35. Spatial periodicities of dewetting structures of the oleo-liquid films are thus easily controlled.<br>
収録刊行物
-
- Journal of Oleo Science
-
Journal of Oleo Science 55 (6), 277-282, 2006
公益社団法人 日本油化学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204090900096
-
- NII論文ID
- 130000055557
-
- NII書誌ID
- AA11503337
-
- ISSN
- 13473352
- 13458957
-
- NDL書誌ID
- 7912462
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可