- A Mineralogical Consideration on Unusual Cracking of Concrete Structures containing Calcareous Aggregate
- セッカイケイ コツザイ オ シヨウシテ イジョウ ヒビワレ ガ ハッセイシタ コウゾウブツ コンクリート ノ コウブツガクテキ コウサツ
この論文をさがす
説明
Many types of unusual cracking occurs in concrete structures containing calcareous aggregates such as limestone or coral reef, but few studies have been conducted on these phenomena.<BR>It has previously been reported that this unusual occurence of cracking in concrete is due to an alkali-carbonate or an alkali-silica reaction which is derived from limestone containing fine clay or silica. However, the calcareous aggregates are produced in Japan contain a small amounts of silica and there are few dolomitic limestone deposits in Japan.<BR>A mineralogical study was therefore conducted on cracked concrete structure contained calcareous aggregates. The results indicated following common characteristics:(1) A large quantity portlandite cement mineral was formed.(2) Cement minerals such as 3CaO·Al2O3·8-12H20 or 4CaO·Al2O3. 3H2O were formed.(3) In cases where of 4CaO·Al2O3·3H2O appeared, gel filled cracks or air babbles were observed.(4) The components of gel, filled cracks and air babbles in concrete originated from within the cement. The gel was a biproduct of a reaction with in cement, and was not responsible for the cracking of concrete by swelling.<BR>It is thought that cracking in concrete contaning calcareous aggregates is caused by swelling, which is due to the formation of large amounts of portlandite and calcium alminate hydrate. It is also thought that this unusual reaction is related to the powder grade of the cement, the water: cement ratio in the concrete or inadequate curing during concrete placement. This study is on going and the results of which will be reported in the near future.
収録刊行物
-
- 粘土科学
-
粘土科学 46 (2), 105-111, 2007
一般社団法人 日本粘土学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204111147392
-
- NII論文ID
- 130004307801
- 110006279504
-
- NII書誌ID
- AN00199972
-
- ISSN
- 21863563
- 04706455
-
- NDL書誌ID
- 8854267
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可