A study of surface modification of steel, Al alloy by ion implantation technique.
-
- ASAHI Naotatsu
- Hitachi Powder Metals Co. Ltd.
-
- HAGINOYA Mitsuo
- Hitachi Research Lab., Hitachi Ltd.
-
- SATOU Tadashi
- Hitachi Research Lab., Hitachi Ltd.
-
- HASHIMOTO Isao
- Kokubu Works, Hitachi Ltd.
Bibliographic Information
- Other Title
-
- イオン注入法による鉄鋼,Al合金の表面改質
Abstract
The effect on the metallurgical structure and wear behavior of Al-Si alloy and steel produced by nitrogen ion implantation and ion beam mixing deposition (simultaneous nitrogen ion implantation and Ti vapor deposition) using an ion beam source were studied. A combination of X-ray diffraction, Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS) was used to determine the metallurgical structure and chemical composition, and to investigate. The chemical bonding state of the ion treated surfaces.<br>X-ray diffraction data showed that TiN films were formed at room temperature by ion beam mixing treatment. It is demonstrated, that a mixing layer was observed between the substrate and TiN film.<br>AlN was observed when nitrogen ions were implanted in Al-Si alloy. The pin-on disk wear test showed a decrease in the coefficient of friction and an increase in wear resistance for surface treated by both nitrogen ion implantation and ion beam mixing.
Journal
-
- Journal of the Metal Finishing Society of Japan
-
Journal of the Metal Finishing Society of Japan 38 (8), 329-333, 1987
The Surface Finishing Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390001204111818368
-
- NII Article ID
- 130003810108
-
- COI
- 1:CAS:528:DyaL2sXlsF2msr0%3D
-
- ISSN
- 18843395
- 00260614
- http://id.crossref.org/issn/00260614
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed