塩化ナトリウム水溶液中におけるアルミニウムの保護電位におよぼすアノード分極からカソード分極への折り返し分極電位の影響
書誌事項
- タイトル別名
-
- Effects of Polarization Turning from Anode to Cathode on Protection Potentials of Aluminum in Sodium Chloride Solutions
- Studies on Aluminum Anode for Cathodic Protection (Part 9)
- 流電陽極用アルミニウム合金に関する研究 (第9報)
この論文をさがす
説明
The effects of protection potentials for aluminum in 0.5N NaCl solutions as functions of the potential turning from anode to cathode and all values of pH of the solutions were reported in the preceding paper.<br>The protection potentials of aluminum were always constant independent of pH values when the border potentials turning from anode to cathode were constantly regulated in 0.5N NaCl solution of pH=4-6, at which an oxide film was produced on the surface of aluminum.<br>The protection potentials in 0.5N NaCl solutions of pH=4, 5.5, and 6 at the up-down border potentials of+50mV (vs. SCE) were -1.45V (vs. SCE), -1.47V (vs. SCE), and -1.39V (vs. SCE), respectively; and the potentials of these solutions at the up-down border potentials of about -500mV (vs. SCE) were -1.20V (vs. SCE), -1.37V (vs. SCE), and -1.20V (vs. SCE), respectively.<br>In the same way, the protection potentials of aluminum in 0.5N NaCl solutions of pH=8 and 10 were affected by the border potentials, but were independent of pH values when the up-down border potentials were regulated, on the assumption that Al2O3⋅H2O was formed on the surface of aluminum at the time when the aluminum was put in the solutions.<br>The protection potentials in 0.5N NaCl solutions of pH=8 at the up-down border potential of+50mV (vs. SCE) and about -500mV (vs. SCE) were -1.36V (vs. SCE) and -1.16V (vs. SCE), respectively; and the potentials in these solutions of pH=10 at the above border potentials were -1.35V (vs. SCE) and -1.16V (vs. SCE), respectively.<br>The approximate flowing currents of aluminum at the above up-down border potentials were nearly constant independent of pH values.<br>In 0.5N NaCl solutions of pH=12, the protection potentials of aluminum were nearly constant, about -1.8V (vs. SCE), independent of the up-down border potentials.
収録刊行物
-
- 金属表面技術
-
金属表面技術 24 (5), 272-275, 1973
一般社団法人 表面技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204113982208
-
- NII論文ID
- 130003994057
-
- ISSN
- 18843395
- 00260614
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可