- Electrodeposition of Nb-Sn Alloy from Ambient-Temperature Molten Salt Electrolytes by Pulse Electrolysis.
- パルス デンセキホウ ニヨル ジョウオンガタ ヨウユウエンヨク カラ ノ Nb
この論文をさがす
抄録
Electrodeposition of Nb-Sn alloy from ambient temperature molten salt electrolytes, i.e., an SnCl2-NbCl5-BPC (1-butylpyridinium chloride) system and an Sn-NbCl5-BPC system, by pulse electrolysis was investigated. The Nb content in the Nb-Sn electrodeposit was effected by the pulse period, current density, and duty ratio. Decreasing the duty ratio and increasing the current density increased the Nb content in the Nb-Sn alloy deposited from a 28.6mol%SnCl2-14.3mol%NbCl5-57.1mol%BPC bath. An Nb-Sn alloy containing 44.3wt% Nb was obtained from this bath at 60mA·cm-2, T=50ms, and a duty ratio of 0.2, An Nb-Sn alloy containing 41.3wt% Nb was deposited from a 7.7mol%Sn-15.4mol%NbCl5-76.9mol%BPC bath at 60mA·cm-2, T=10ms, and a duty ratio of 0.2.
収録刊行物
-
- 表面技術
-
表面技術 48 (4), 454-459, 1997
一般社団法人 表面技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204114476544
-
- NII論文ID
- 10002258941
-
- NII書誌ID
- AN1005202X
-
- ISSN
- 18843409
- 09151869
-
- NDL書誌ID
- 4184941
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可