Electrodeposition of Iron from Sulfamate Baths Containing Ammonium Bifluoride
-
- HAYASHI Teiichi
- Government Industrial Research Institute, Nagoya
-
- UENO Hiroshi
- Government Industrial Research Institute, Nagoya
-
- TAKAGI Shushi
- Government Industrial Research Institute, Nagoya
-
- MIWA Shigeru
- Government Industrial Research Institute, Nagoya
Bibliographic Information
- Other Title
-
- 酸性フッ化アンモニウム添加のスルファミン酸浴による鉄電着
- Electrodeposition of Iron from Sulfamic acid Baths (Part 2)
- スルファミン酸浴による鉄電着 (第2報)
Search this article
Description
The effect of ammonium bifluoride as an addition agent to the bath composed of ferrous sulfamate and sulfamic acid for iron deposition was studied.<br>Furthermore, the effects of the concentration of ferrous ion, amount of the addition agent, pH, cathodic current density, and bath temperature on current efficiency and surface state of the deposited iron were also investigated.<br>As the results, the optimum conditions found were as follows.<br>Bath composition: ferrous ion 95g/l<br>saccharin 0.1g/l<br>ammonium bifluoride 10g/l<br>pH3.0<br>Depositing conditions: bath temperature 60-70°C<br>cathodic current density 5-10Amp./dm2<br>Under the above conditions, the current efficiency was 75-85% and the deposition rate was varied with the current efficiency, but was calculated to be in the range of 40-110μ/hr. The throwing power of the bath was nearly equal to that of copper sulfate bath.<br>The deposit of up to 0.5mm thick had a non-bright rugged surface, but its structure showed uniform appearance with no cracks or pits. Therefore, the addition agent, ammonium bifluoride, had an effect of preventing cracks or pits, but no effect on improving brightness.
Journal
-
- Journal of the Metal Finishing Society of Japan
-
Journal of the Metal Finishing Society of Japan 21 (5), 253-258, 1970
The Surface Finishing Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390001204115087360
-
- NII Article ID
- 130003993891
-
- ISSN
- 18843395
- 00260614
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed