Tribological Properties of Nitrogen Ion Implanted Ti Alloy.
-
- ITOH Yoshihiko
- TOYOTA Central Res. and Dev. Labs., Inc.
-
- ITOH Akio
- TOYOTA Central Res. and Dev. Labs., Inc.
-
- AZUMA Hirozumi
- TOYOTA Central Res. and Dev. Labs., Inc.
-
- HIOKI Tatumi
- TOYOTA Central Res. and Dev. Labs., Inc.
Bibliographic Information
- Other Title
-
- 窒素イオン注入したTi合金のトライボロジー特性
- チッソ イオン チュウニュウシタ Ti ゴウキン ノ トライボロジー トクセイ
Search this article
Abstract
In order to investigate the mechanical properties of ion-implanted Ti alloy (Ti-6Al-4V), disk samples of Ti-6Al-4V were implanted with 200keV N2+ ions at doses of 2.5×1016 to 5×1017 ions/cm2. Tribological properties were evaluated with pin-on-disk tests. Bearing steel (SUJ2) balls 5mm in diameter were used as pins. Sliding conditions were as follows: load, 0.46N; speed, 0.04m/s; oil lubrication, SAE 7.5W-30.<br>Knoop hardness (load: 98mN) increased from Hk 356 to Hk 556 (dose: 5×1017ions/cm2) with ion dosage. The coefficient of friction of N2+ ion-implanted Ti-6Al-4V disks ranged from 0.1 to 0.2, values that were lower than 0.6 obtained for an unimplanted disk. N2+ ion implantation reduced wear on the pins as well as on the Ti-6Al-4V disks. The seizure load of N2+ ion-implanted disks increased with ion dosage.
Journal
-
- Journal of The Surface Finishing Society of Japan
-
Journal of The Surface Finishing Society of Japan 47 (4), 345-348, 1996
The Surface Finishing Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390001204115169280
-
- NII Article ID
- 10002256142
- 10011869308
-
- NII Book ID
- AN1005202X
-
- ISSN
- 18843409
- 09151869
-
- NDL BIB ID
- 3947925
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed