  • Effect of Nitriding Conditions on Surface Hardening of Nickel Alloy by a Plasma Nitriding Process.
  • イオン チッカホウ ニ ヨル ニッケル ゴウキン ノ ヒョウメン コウカ ニ

この論文をさがす

説明

In order to investigate the effect of nitriding conditions on the hardness and thickness of the nitrided layer in nickel alloys, a tentative nickel binary alloy of Ni-30wt%Cr was nitrided in plasma nitriding at different nitriding temperatures ranging from 673 to 1073K nitriding times of 3.6 to 32.4ks, nitrogen gas concentrations in N2+H2 mixed gas of 10 to 100vol%, gas pressures of 270 to 1330Pa, discharge voltages of 270 to 420V and current densities of 14.2 to 19.5A/m2.<br>Nitriding temperature was the parameter that affected the hardness of the nitrided layer. The maximum surface hardness was Hv 760 at a nitriding temperature of 823K. The thickness of the nitrided layer depended on the nitriding temperature, nitriding time, and nitrogen gas concentration. Gas pressure, discharge voltage, and discharge current density, however, did not affect surface hardening in the nickel alloy.<br>In this study, we determined that the optimum nitriding conditions for surface hardening of nickel alloys by plasma nitriding were temperature at 823K and 90vol%N2+ 10vol%H2 mixed gas atmosphere at 800Pa.

収録刊行物

  • 表面技術

    表面技術 46 (2), 155-161, 1995

    一般社団法人 表面技術協会

参考文献 (12)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ