- X-ray Diffraction Analysis and Cyclic Voltammograms on the Surface of C/C Composites Prepared Using PAN-Based Fiber at Different Heat Treatment Temperatures.
- ネツ ショリ オンド オ カエタ PANケイ C C コンポジット ヒョウメン
この論文をさがす
抄録
The correlation between the redox behavior of surface compounds formed in dilute sulfuric acid and the heat treatment temperature (HTT) of 2 D-C/C composites whose fibers are made of PAN was investigated by using X-ray diffraction analysis (XRD) and cyclic voltammetry (CV). XRD results indicate that the reflection intensity increased with HTT but that the half-value width decreased. These results suggest that the graphite structure developed with increasing HTT. Cyclic voltammograms were measured for both x-y planes parallel to woven laminates and x-z planes perpendicular to these. For both planes, the current corresponding to the formation of phenol-type compounds (at 0.3V-0.4V) was suppressed with increasing HTT, i.e, the graphite structure development. The anodic currents between 0.3V and 0.4V for the x-z plane at the same HTT was lower than those for the x-y plane. The current corresponding to the formation of carbonyl compounds (at 0.8V), in contrast increased with HTT. The reduction current observed from 1.0V increased with decreasing HTT.
収録刊行物
-
- 表面技術
-
表面技術 47 (7), 633-637, 1996
一般社団法人 表面技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204115778560
-
- NII論文ID
- 10002256840
-
- NII書誌ID
- AN1005202X
-
- ISSN
- 18843409
- 09151869
-
- NDL書誌ID
- 3995265
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可