冷間金型用合金工具鋼へのPVDコーティングのための前処理

DOI 被引用文献1件 参考文献5件

書誌事項

タイトル別名
  • Pretreatment Prior to PVD Coating of the Surface of Cold Working Die Steel

抄録

This study investigated pretreatment for PVD coating onto cold working die steel corresponding to SKD11. The roughness and height of the carbide of the SKD11 surface increased concomitantly with increasing etching times by both Cr and Ar ion bombardment. The CrN coating adhesion onto the SKD11 changes to the worth, when the carbide thickness was greater than 150 nm. Electron beam irradiation of the SKD11 surface produced about 5-μm-thick melted layers having a smooth surface and improved the CrN adhesion. Furthermore, the corrosion resistance of the CrN coated onto the SKD11 improved after electron beam irradiation.

収録刊行物

  • 表面技術

    表面技術 64 (12), 677-681, 2013

    一般社団法人 表面技術協会

被引用文献 (1)*注記

もっと見る

参考文献 (5)*注記

もっと見る

キーワード

詳細情報 詳細情報について

  • CRID
    1390001204117138560
  • NII論文ID
    130004704930
  • DOI
    10.4139/sfj.64.677
  • COI
    1:CAS:528:DC%2BC2cXjtFarsrc%3D
  • ISSN
    18843409
    09151869
  • 本文言語コード
    ja
  • データソース種別
    • JaLC
    • Crossref
    • CiNii Articles
  • 抄録ライセンスフラグ
    使用不可

問題の指摘

ページトップへ