プリント配線板用腐食防止剤としてのミセル水溶液から形成した1-オクタデカンチオール自己組織化単分子膜の実用化検討

DOI Web Site 参考文献20件

書誌事項

タイトル別名
  • Practical Use of 1-octadecanethiol Self-assembly Monolayers Obtained from Aqueous Micellar Solution as Corrosion Inhibitor for Printed Wiring Boards
  • プリント ハイセンバンヨウ フショク ボウシザイ ト シテ ノ ミセル スイヨウエキ カラ ケイセイ シタ 1-オクタデカンチオール ジコ ソシキカタンブンシマク ノ ジツヨウカ ケントウ

この論文をさがす

抄録

A 1-octadecanethiol self-assembly monolayer（ODT-SAM）was formed on electroless Au/Ni-P layers to improve corrosion resistance. However, ethanolic solutions are inferior to aqueous solution in terms of safety and cost. For this study, ODT-SAMs were obtained from aqueous solutions. A nonionic surfactant was used to dissolve ODT in water. The adsorption of ODT was evaluated based on the contact angle of water. The corrosion resistance was evaluated using the salt spray test. The corrosion resistance of ODT-SAMs obtained by immersion for 300 s in an aqueous micellar solution of the surfactant concentration of at least 2.3 × 10－1 mol/L and the ODT concentration of 5.0 × 10－3 mol/L was equival ent to that of ODT-SAMs from ethanolic solutions. The formation status of the ODT-SAMs was examined using infrared reflection absorption spectroscopy. The structure of ODT-SAMs on a gold plated surface in an aqueous micellar solution was compared to that of ODT-SAMs on a gold plated surface in an ethanol solution, revealing no difference. No deterioration in bondability was observed when the solder-ball bondability and wire bondability of an Au/Ni-P substrate on which ODT-SAMs obtained from an aqueous micellar solution were formed. Results show that ODT-SAMs obtained from aqueous micellar solutions are useful as corrosion inhibitors for electroless Au/Ni-P layers used in printed wiring boards.

収録刊行物

  • 表面技術

    表面技術 64 (2), 140-145, 2013

    一般社団法人 表面技術協会

参考文献 (20)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ