Mössbauer and DTA Studies of Superionic Conducting AgCl–Ag2O–B2O3 Glasses

書誌事項

タイトル別名
  • Moessbauer and DTA studies of superionic conducting AgCl-Ag2O-B2O3 glasses.

この論文をさがす

説明

A structural study of silver borate glasses containing 20 or 30 mol% AgCl and 1 mol% Fe2O3 has been performed by means of Mössbauer spectroscopy. The distinct decreases in the Mössbauer parameters observed in the borate glasses with Ag2O contents higher than about 10 mol% suggest that chloride ions are covalently bonded with tetrahedral iron or boron atoms as nonbridging chlorine. On the other hand, chloride ions are considered to be ionically bonded with Ag+ ions at the interstitial sites of the three-dimensional network composed of BO3, BO4, and FeO4 units when the Ag2O content is lower than 10 mol%. Measurements of the glass transition temperatures and the electric conductivity show a good agreement with the Mössbauer results, suggesting that mobile and electric conducting Ag+ ions change their configurational sites from the interstitial sites which are close to Cl ions to different interstitial sites which are close to the nonbridging chlorine atom.

収録刊行物

被引用文献 (3)*注記

もっと見る

参考文献 (30)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ