BCSJ Award Article : Li₄B₄M₃O₁₂Cl (M = Al, Ga) : An Electrochemically Stable, Lithium-Ion-Conducting Cubic Boracite with Substituted Boron Sites
-
- Kajihara Koichi
- Department of Applied Chemistry, Graduate School of Urban Environmental Sciences, Tokyo Metropolitan University
-
- Tezuka Naoto
- Department of Applied Chemistry, Graduate School of Urban Environmental Sciences, Tokyo Metropolitan University
-
- Shoji Mao
- Department of Applied Chemistry, Graduate School of Urban Environmental Sciences, Tokyo Metropolitan University
-
- Wakasugi Jungo
- Department of Applied Chemistry, Graduate School of Urban Environmental Sciences, Tokyo Metropolitan University
-
- Munakata Hirokazu
- Department of Applied Chemistry, Graduate School of Urban Environmental Sciences, Tokyo Metropolitan University
-
- Kanamura Kiyoshi
- Department of Applied Chemistry, Graduate School of Urban Environmental Sciences, Tokyo Metropolitan University
書誌事項
- タイトル別名
-
- Li<sub>4</sub>B<sub>4</sub><i>M</i><sub>3</sub>O<sub>12</sub>Cl (<i>M</i> = Al, Ga): An Electrochemically Stable, Lithium-Ion-Conducting Cubic Boracite with Substituted Boron Sites
- Li4B4<i>M</i>3O12Cl (<i>M</i> = Al, Ga): An Electrochemically Stable, Lithium-Ion-Conducting Cubic Boracite with Substituted Boron Sites
この論文をさがす
抄録
<p>A cubic boracite with substituted boron sites, Li4B4M3O12Cl (M = Al, Ga), derived by fully replacing the tetrahedral BO4 units in the parent lithium chloroboracite, Li4B7O12Cl, with AlO4 or GaO4 units, has been discovered. These substituted compounds have the largest unit cell dimensions of known boracites and are formed as the stable primary phase in highly crystalline glass-ceramics derived from the Li2O–B2O3–M2O3–LiCl quarternary system. The conductivity of Li4B4M3O12Cl glass-ceramics at room temperature was ∼10−5 S cm−1, an order of magnitude larger than the highest conductivity recorded for Li4B7O12Cl glass-ceramics. The Li4B4Al3O12Cl glass-ceramic is stable in contact with Li metal and exhibits a wide electrochemical window between 0 and 6 V vs. Li/Li+ and a Li+ ion transport number of ∼1.</p>
収録刊行物
-
- Bulletin of the Chemical Society of Japan
-
Bulletin of the Chemical Society of Japan 90 (12), 1279-1286, 2017
公益社団法人 日本化学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204143688320
-
- NII論文ID
- 130006250361
-
- NII書誌ID
- AA00580132
-
- ISSN
- 13480634
- 00092673
-
- NDL書誌ID
- 028707533
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可