Erratum: “Point Defect Clusters in Electron-Irradiated Gold”
-
- Yoshida Naoaki
- Department of Material Physics, Faculty of Engineering Science, Osaka University
-
- Kiritani Michio
- Department of Material Physics, Faculty of Engineering Science, Osaka University
書誌事項
- タイトル別名
-
- Point Defect Clusters in Electron-Irradiated Gold
この論文をさがす
抄録
Defect formation in gold by the irradiation of 2.0∼2.5 MeV electrons was studied with a high voltage electron microscope. The formation of dislocation loops by the aggregation of interstitials generally precedes the formation of the defects by vacancies. Permanent sinks, such as specimen surfaces and dislocations, prevent the formation of interstitial type of defects and enhance the formation of vacancy clustered defects. A rapid formation of the vacancy type defects and the simultaneous shrinkage of interstitial type loops after the cessation of the irradiation are observed. Kinetics analysis of the point defect behaviour, standing on the random migration of interstitials and vacancies, explains all the observed various phenomena as the competition processes between two kinds of point defects under various circumstances. The irradiation intensity dependence of the density of interstitial type defects shows that the di-interstitials are their stable nucleus.
収録刊行物
-
- Journal of the Physical Society of Japan
-
Journal of the Physical Society of Japan 35 (5), 1418-1429, 1973
一般社団法人 日本物理学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204187320576
-
- NII論文ID
- 210000083934
- 130003893884
- 110001974781
- 210000084023
- 130003893936
-
- NII書誌ID
- AA00704814
-
- COI
- 1:CAS:528:DyaE3sXlsFSmsbs%3D
-
- ISSN
- 13474073
- 00319015
-
- NDL書誌ID
- 7669261
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可