Radiophotoluminescence centers of silver-activated phosphate glass
-
- Yokota Ryosuke
- Central Research Laboratory, Tokyo Shibaura Electric Co., Ltd.
-
- Imagawa Hiroshi
- Central Research Laboratory, Tokyo Shibaura Electric Co., Ltd.
書誌事項
- タイトル別名
-
- Radiophotoluminescent Centers in Silver-Activated Phosphate Glass
- Radiophotoluminescence centers in silver-activated phosphate glass
この論文をさがす
抄録
ESR studies of radiophotoluminescence (RPL) centers in silver-activated phosphate glass were performed after the glasses had been γ-irradiated at 77°K. It is shown that the silver ions act as traps for both electrons and positive holes. By the separate formation of electron-trapped silver centers and hole-trapped silver center, it was verified that all these silver centers act as RPL centers. It was found that a positive hole in PO4 tetrahedron is transfered to Ag+ ion and this process is the main reason of RPL build-up. Stabilization phenomenon of RPL centers was found. It was found that alkali and or silver ion migration is necessary for stabilization. The reason why RPL in these glasses has high stability and builds-up after γ-irradiation was clarified. The resonances which are considered due to exchange coupled pairs, triads and higher aggregates of electron-trapped silver centers were found.
収録刊行物
-
- Journal of the Physical Society of Japan
-
Journal of the Physical Society of Japan 23 (5), 1038-1048, 1967
一般社団法人 日本物理学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204191352576
-
- NII論文ID
- 210000079918
- 110001974051
-
- NII書誌ID
- AA00704814
-
- BIBCODE
- 1967JPSJ...23.1038Y
-
- COI
- 1:CAS:528:DyaF1cXksVGnug%3D%3D
-
- ISSN
- 13474073
- 00319015
-
- NDL書誌ID
- 8501444
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可