Phase Decomposition in a Ti-13Nb-13Zr Alloy during Aging at 600°C
-
- Kobayashi Sengo
- Department of Materials Science and Engineering, Ehime University
-
- Nakagawa Shintaro
- Department of Materials Science and Engineering, Ehime University
-
- Nakai Kiyomichi
- Department of Materials Science and Engineering, Ehime University
-
- Ohmori Yasuya
- Department of Materials Science and Engineering, Ehime University
Bibliographic Information
- Other Title
-
- Phase Decomposition in a Ti 13Nb 13Zr Alloy during Aging at 600ドC
- Phase Decomposition in a Ti-13Nb-13Zr Alloy during Aging at 600°C
Search this article
Description
Phase decomposition in a Ti–13 mass%Nb–13 mass%Zr alloy during isothermal aging at 600°C has been investigated by means of transmission electron microscopy and Vickers hardness measurements. Specimens solution-treated at 1000°C in β phase field were quenched and aged at 600°C in (α+β) region. Beta phase was fully transformed into martensitic α′ laths by quenching from 1000°C. Formation of β phase on tempered α′ lath interfaces occurred during aging. Early in the stage of aging, β phase transformed into α′′ martensite completely by quenching. As increasing in aging time, athermal ω phase was formed in β phase by quenching. Beta phase was stabilized by prolonged aging. Enrichment of Nb content into β phase occurred with increasing in aging time, resulting in the formations of athermal ω phase and (α+β) two-phase structure. The hardness increased with the ω phase formation in β phase, followed by the decrease of hardness due to suppression of ω phase formation induced by enrichment of Nb in β phase.
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (12), 2956-2963, 2002
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001204245554176
-
- NII Article ID
- 10012328653
-
- NII Book ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3sXhtF2nurY%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL BIB ID
- 6394940
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed