A Relationship between Glass-Forming Ability and Reduced Glass Transition Temperature near Eutectic Composition
-
- Li Y.
- Department of Materials Science, Science Faculty, National University of Singapore
書誌事項
- タイトル別名
-
- Relationship between Glass Forming Ability and Reduced Glass Transition Temperature near Eutectic Composition
この論文をさがす
抄録
Onset temperature (solidus), Tm and offset temperature (liquidus) Tl of melting of a series of bulk glass forming alloys based on Zr, La, Mg, Pd and rare-earth elements have been measured by studying systematically the melting behaviour of these alloys using differential thermal analysis (DTA) or differential scanning calorimetry (DSC). Bulk metallic glass formation has been found to be most effective at or near their eutectic points and less effective for off-eutectic alloys. Reduced glass transition temperature Trg given by Tg⁄Tl is found to show a stronger correlation with critical cooling rate or critical section thickness for glass formation than Trg given by Tg⁄Tm.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 42 (4), 556-561, 2001
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204245567232
-
- NII論文ID
- 10006547974
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3MXktlKjs7s%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 5764490
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可