Relationship between Deformation and Recrystallization in Σ3 Isoaxial Aluminum Bicrystal Deformed in Tension along the <011> Axis
-
- Kashihara Keizo
- Wakayama National College of Technology
-
- Tagami Minoru
- Faculty of Engineering, The University of Tokushima
-
- Tanaka Hiroshi
- Wakayama National College of Technology
-
- Okada Tatsuya
- Faculty of Engineering, The University of Tokushima
-
- Inoko Fukuji
- Faculty of Engineering, The University of Tokushima
書誌事項
- タイトル別名
-
- Relationship between Deformation and Recrystallization in <I>Σ</I><B>3</B> Isoaxial Aluminum Bicrystal Deformed in Tension along the <<B>011</B>> Axis
- Relationship between Deformation and Recrystallization in シグマ 3 Isoaxial Aluminum Bicrystal Deformed in Tension along the 011 Axis
- Relationship between Deformation and Recrystallization in <I>Σ</I><B>3</B> Isoaxial Aluminum Bicrystal Deformed in Tension along the <<B>011</B>> Axis
この論文をさがす
抄録
Deformation and recrystallization behaviors were examined using a Σ3 isoaxial aluminum bicrystal specimen deformed in tension along the ⟨011⟩ axis. At a tensile strain of 20%, an inhomogeneously deformed structure was developed near the GB . The recrystallization at the GB was dominated by the strain-induced grain boundary migration (SIBM). The strong edge components of piled-up dislocations contributed the occurrence of the SIBM, whereas the screw dislocations moved into the GB from both component crystals were considered to pass through or canceled each other in the GB, because of the special orientational and geometric conditions in the crystals.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 42 (3), 381-384, 2001
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204245907456
-
- NII論文ID
- 130004451439
- 10006547294
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3MXjtlSjsbY%3D
-
- ISSN
- 13475320
- 13459678
- http://id.crossref.org/issn/09161821
-
- NDL書誌ID
- 5727182
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可