Corrosion Behavior of Zr–(Nb–)Al–Ni–Cu Glassy Alloys
-
- Pang Shujie
- Institute for Materials Research, Tohoku University
-
- Zhang Tao
- Institute for Materials Research, Tohoku University
-
- Kimura Hisamichi
- Institute for Materials Research, Tohoku University
-
- Asami Katsuhiko
- Institute for Materials Research, Tohoku University
-
- Inoue Akihisa
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Corrosion Behavior of Zr–(Nb–)Al–Ni–Cu Glassy Alloys
この論文をさがす
抄録
The melt-spun glassy Zr60−xNbxAl10Ni10Cu20 (x=0, 5, 10, 15, 20 at%) alloys were found to exhibit a large supercooled liquid region (ΔTx) exceeding 42 K before crystallization. The largest ΔTx for the glassy alloys containing Nb reaches as large as 82 K for the Zr55Nb5Al10Ni10Cu20 alloy. The glass transition temperature (Tg) increases and the ΔTx value decreases with increasing Nb content. The corrosion behavior of the Zr–(Nb)–Al–Ni–Cu glassy alloys was examined by mass loss (=weight loss) and electrochemical measurements. In 1N HCl solution at 298 K, the addition of Nb for replacing some portion of Zr is effective in improving the corrosion resistance of the investigated Zr-based glassy alloys. The corrosion rate significantly decreases with increasing Nb content. The pitting potential and open circuit potential rise with Nb content. In 3%NaCl solution, the addition of Nb effectively increases the pitting potentials of the glassy alloys. In 1N H2SO4 solution, the corrosion rates of the glassy alloys are 10−4∼10−3 mm·y−1 (1 mm·y−1=0.317 pm·s−1). They are spontaneously passivated and have a wide passive region with significantly low passive current density. The open circuit potential increases with an increase in Nb content.
収録刊行物
-
- Materials Transactions, JIM
-
Materials Transactions, JIM 41 (11), 1490-1494, 2000
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204246266240
-
- NII論文ID
- 130003557323
- 10005354248
-
- NII書誌ID
- AA10699969
-
- COI
- 1:CAS:528:DC%2BD3MXnsFSmtw%3D%3D
-
- ISSN
- 2432471X
- 09161821
- http://id.crossref.org/issn/09161821
-
- NDL書誌ID
- 5574941
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可