Formation, Thermal Stability and Mechanical Properties in Zr-Al-Co Bulk Glassy Alloys
-
- Wada Takeshi
- Graduate School, Tohoku University
-
- Zhang Tao
- Institute for Materials Research, Tohoku University
-
- Inoue Akihisa
- Institute for Materials Research, Tohoku University
Search this article
Abstract
A Zr–Al–Co ternary alloy was investigated in order to clarify the glass-forming ability, thermal stability and mechanical properties. The Zr55Al20Co25 alloy was found to be fabricated in bulk glassy alloy rods with diameters up to at least 2.5 mm. The glassy alloy rod of 2.5 mm in diameter exhibits a large supercooled liquid region of 79 K, followed by a nearly single exothermic peak due to the precipitation of ZrCo+ZrAlCo+Zr6Al2Co phases. The glassy alloy rod exhibits Young’s modulus of 114 GPa, high compressive fracture strength of 1900 MPa and total fracture elongation of 1.7%. The finding of forming the bulk glassy alloy at the new ternary composition of Zr55Al20Co25 by the copper mold casting method is encouraging for future search of a new glassy alloy composition.
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (11), 2843-2846, 2002
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001204246315648
-
- NII Article ID
- 130004451733
- 10012328221
-
- NII Book ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3sXjtFGl
-
- ISSN
- 13475320
- 13459678
-
- NDL BIB ID
- 6367485
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed