Formation of Mg2Ni from Mg and Ni Powder Mixtures by the Use of a Planetary Ball Mill
-
- Mi Guomin
- Institute for Advanced Materials Processing, Tohoku University
-
- Saito Fumio
- Institute for Advanced Materials Processing, Tohoku University
書誌事項
- タイトル別名
-
- Formation of Mg<SUB>2</SUB>Ni from Mg and Ni Powder Mixtures by the Use of a Planetary Ball Mill
- Formation of Mg2Ni from Mg and Ni Powde
この論文をさがす
抄録
Mg2Ni powder material can be synthesized from a mixture of Mg and Ni by its mechanical alloying using a planetary ball mill. The particle size of the mechanically alloyed Mg2Ni powder decreases with an increase in milling time, and the Mg2Ni phase in the milled mixture tends to change into poor crystalline structure in the prolonged milling operation. No significant exothermic reaction takes place during heating of the mechanically alloyed Mg2Ni powder except for the recrystallizing reaction at 430 K, while a considerable exothermic reaction due to the self-combustion is detected at around 860 K for the unmilled mixture followed by the ignition behavior of the starting powders at 780 K. There is no significant difference in the characteristic of hydrogen storage in the PCT diagram between the mechanically alloyed Mg2Ni powder and the thermally synthesized one.
収録刊行物
-
- Materials Transactions, JIM
-
Materials Transactions, JIM 39 (8), 810-813, 1998
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204246718592
-
- NII論文ID
- 130003557073
- 10003803424
-
- NII書誌ID
- AA10699969
-
- COI
- 1:CAS:528:DyaK1cXms1OntrY%3D
-
- ISSN
- 2432471X
- 09161821
-
- NDL書誌ID
- 4549320
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可