Model Calculation of the Damage Rate Dependence of Yield Stress Change in an Irradiated Fe-Cu Model Alloy
-
- Yanagita Seiya
- Research Reactor Institute, Kyoto University
-
- Xu Qiu
- Research Reactor Institute, Kyoto University
-
- Yoshiie Toshimasa
- Research Reactor Institute, Kyoto University
-
- Ino Hiromitsu
- College of Engineering, Hosei University
この論文をさがす
抄録
The damage rate dependence of the yield stress change in a neutron-irradiated Fe–Cu model alloy was analyzed by a model calculation. The model was based on the rate theory, and focused on the description of the nucleation and growth of point defect clusters and copper clusters. The binding between copper atoms and vacancies and the effect of cascade damage which directly creates small point defect clusters were incorporated in this model. The instability of small point defect clusters caused by thermal dissociation was also included. From the result of the calculation, the yield stress changes were estimated using the Orowan model and the Russel-Brown model. As a result of this calculation, it was clarified that copper clusters are the main factor of yield stress change in almost all irradiation stages below 0.1 dpa. The contribution of copper clusters to yield stress change increased with decreasing damage rate. The nature of the damage rate dependence is not affected by the copper-vacancy binding but by the sink strength, which changes dynamically throughout irradiation.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (7), 1663-1669, 2002
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204246816512
-
- NII論文ID
- 130004451880
- 10012325476
- 30018849784
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD38Xmt1equ7Y%3D
-
- ISSN
- 13475320
- 13459678
- http://id.crossref.org/issn/09161821
-
- NDL書誌ID
- 6241160
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可