High Temperature Deformation and Fracture Behaviour of Continuous Alumina Fiber Reinforced Aluminum Composites with Different Fiber Orientation
-
- Matsuda Norio
- Department of Mechanical Systems Engineering, Faculty of Engineering, Yamagata University
-
- Matsuura Keisuke
- Department of Mechanical Systems Engineering, Faculty of Engineering, Yamagata University
書誌事項
- タイトル別名
-
- High Temperature Deformation and Fractu
この論文をさがす
抄録
Deformation and fracture behaviours were investigated in a continuous alumina fiber reinforced aluminum composite by tensile tests of specimens with different tensile axis orientations to the fiber axis at various temperatures from room temperature to 773 K. The orientation dependence of the tensile strength is well described by the maximum stress theory as well as by the Tsai-Hill’s theory.<BR>Temperature dependences of strength σc of composite in the direction of fiber axis, shear strength τu of the matrix along the fiber axis and tensile strength σu of the matrix in the direction normal to the fiber axis were determined. It is concluded that the decrease in the tensile strength of the composite with the rise of temperature is mainly due to the decrease in the τu and σu. It is suggested from the observation of fracture surfaces that the decrease in τu and σu at high temperatures is not only due to the decrease in strength of the matrix, but partly to the lowered shear and tensile strength of the matrix-fiber interface.
収録刊行物
-
- Materials Transactions, JIM
-
Materials Transactions, JIM 38 (3), 205-214, 1997
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204247111296
-
- NII論文ID
- 130003556898
- 10002452010
-
- NII書誌ID
- AA10699969
-
- COI
- 1:CAS:528:DyaK2sXjtVOiu7k%3D
-
- ISSN
- 2432471X
- 09161821
-
- NDL書誌ID
- 4209535
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可