Effect of Tungsten on Mechanical Properties of High-Purity 60 mass%Cr-Fe Alloys
-
- Totouge Masayuki
- Institute for Materials Research, Tohoku University
-
- Harima Nobuyuki
- Institute for Materials Research, Tohoku University
-
- Takaki Seiichi
- Institute for Materials Research, Tohoku University
-
- Abiko Kenji
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Effect of Tungsten on Mechanical Properties of High Purity 60 massパーセント Cr Fe Alloys
この論文をさがす
抄録
The effect of the tungsten addition on the mechanical properties of high-purity 60 mass%Cr–Fe alloy was investigated. High-purity 60 mass%Cr–Fe-4 mass%W alloy ingots were prepared by melting in a newly designed high-frequency induction furnace equipped with a cold copper crucible. The purity of the ingots were higher than 99.98 mass% after the analysis of 21 elements. The deformability at temperatures of 1273 to 1573 K and the tensile properties between 293 K and 1073 K were measured by Gleeble test and tensile test. It was found that the tensile strength of 60 mass%Cr–Fe-4 mass%W alloy is higher than that of 60 mass%Cr–Fe alloy, and the addition of tungsten is effective in improving tensile properties of a 60 mass%Cr–Fe alloy.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (2), 141-146, 2002
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204247245952
-
- NII論文ID
- 130004451762
- 10012320706
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD38XivVCjsbo%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6085566
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可