Effect of Carbon Addition on Solidification Structure and Strength of Cu-Cr In Situ Composite
-
- Mihara Kuniteru
- National Research Institute for Metals
-
- Takeuchi Takao
- National Research Institute for Metals
-
- Suzuki Hirowo G.
- National Research Institute for Metals
書誌事項
- タイトル別名
-
- Effect of Carbon Addition on Solidification Structure and Strength of Cu–Cr <I>In Situ</I> Composite
- Effect of Carbon Addition on Solidifica
- Effect of Carbon Addition on Solidification Structure and Strength of Cu–Cr <I>In Situ</I> Composite
この論文をさがす
説明
A small amount of carbon was doped into a Cu-15 mass%Cr in situ composite to increase the strength of the material. It is found that in the as-cast state Cr dendrites exhibit a needle shape, which can be deformed into fibers much easier than the equiaxial one.<BR>A SIMS analysis with the aid of thermodynamic simulation analysis suggests that Cr carbide exists as a nucleation site of Cr dendrites. The composite has a tensile strength of 1200 MPa and an electrical conductivity of 38% IACS in the cold-worked state, and 960 MPa and 73% IACS after optimized aging treatment.
収録刊行物
-
- Materials Transactions, JIM
-
Materials Transactions, JIM 39 (11), 1093-1100, 1998
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204247819776
-
- NII論文ID
- 130003422537
- 10003804531
-
- NII書誌ID
- AA10699969
-
- COI
- 1:CAS:528:DyaK1MXjvVCgtg%3D%3D
-
- ISSN
- 2432471X
- 09161821
-
- NDL書誌ID
- 4606282
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可