Hydrogen Evolution Characteristics of Sputter-Deposited Co–Mo, Co–Al and Co–Mo–Al Alloy Electrodes in NaOH Solution
-
- Aihara Toshio
- Institute for Materials Research, Tohoku University
-
- Kawashima Asahi
- Institute for Materials Research, Tohoku University
-
- Akiyama Eiji
- Institute for Materials Research, Tohoku University
-
- Habazaki Hiroki
- Institute for Materials Research, Tohoku University
-
- Asami Katsuhiko
- Institute for Materials Research, Tohoku University
-
- Hashimoto Koji
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Hydrogen Evolution Characteristics of Sputter-Deposited Co–Mo, Co–Al and Co–Mo–Al Alloy Electrodes in NaOH Solution
- Hydrogen Evolution Characteristics of S
この論文をさがす
説明
Binary Co–Mo and Co–Al, and ternary Co–Mo–Al alloy electrodes for hydrogen evolution were prepared by using sputter deposition on a nickel substrate with good adhesion. The hydrogen evolution reaction (HER) of these alloy electrodes in the deaerated 1 kmol·m−3 NaOH at 303 K is enhanced significantly compared with pure cobalt electrode. The effective surface area of these alloy electrodes estimated from ac impedance technique is largely increased by leaching of aluminum into alkaline solution. The electrocatalytic activity sequence is Co–Mo–Al>Co–Mo>Co–Al. The maximum activity is obtained for Co–10Mo–58Al alloy with a hydrogen overpotential as low as 110 mV at 103 A·m−2. The enhancement of HER is attributed to both the synergistic effect of alloy constituents and the large effective surface area.
収録刊行物
-
- Materials Transactions, JIM
-
Materials Transactions, JIM 39 (10), 1017-1023, 1998
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204248052224
-
- NII論文ID
- 10003804267
-
- NII書誌ID
- AA10699969
-
- COI
- 1:CAS:528:DyaK1MXnsFyr
-
- ISSN
- 2432471X
- 09161821
-
- NDL書誌ID
- 4587174
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可