Hydrogen-Induced Vacancy Generation Phenomenon in Pure Pd

DOI Web Site Web Site 被引用文献4件 参考文献30件
  • Sakaki Kouji
    Department of Materials Science and Engineering, Osaka University
  • Yamada Tomoyasu
    Department of Materials Science and Engineering, Osaka University
  • Mizuno Masataka
    Department of Materials Science and Engineering, Osaka University
  • Araki Hideki
    Department of Materials Science and Engineering, Osaka University
  • Shirai Yasuharu
    Department of Materials Science and Engineering, Osaka University

この論文をさがす

説明

Lattice defects induced by hydriding in pure Pd have been studied by means of positron lifetime spectroscopy. Component analyses of positron lifetime spectra show that a surprising amount of vacancies together with dislocations are generated by the hydriding at room temperature. Vacancy migration in pure Pd after hydriding is observed around 378 K . Dislocations are much more stable and its migration is observed around 873 K . During the vacancy recovery process, secondary defects, that is, dislocation loops are formed.