Phase Equilibrium between Iron-Silicate Base Slag and Nickel-Iron Matte at 1573K under High Partial Pressures of SO2
-
- Font Jonkion M.
- Institute for Advanced Materials Processing, Tohoku University
-
- Takeda Yoichi
- Department of Materials Science and Technology, Faculty of Engineering, Iwate University
-
- Itagaki Kimio
- Institute for Advanced Materials Processing, Tohoku University
書誌事項
- タイトル別名
-
- Phase Equilibrium between Iron-Silicate Base Slag and Nickel-Iron Matte at 1573 K under High Partial Pressures of SO<SUB>2</SUB>
- Phase Equilibrium between Iron-Silicate
この論文をさがす
説明
As a fundamental study for the oxygen-blowing nickel smelting, the phase equilibrium between iron-silicate base slag saturated with silica and Ni3S2–FeS matte in a magnesia crucible was investigated at 1573 K under the partial pressures of SO2 controlled at 10.1, 50.7 and 101.3 kPa, using a sulfur reservoir for controlling the partial pressure of S2. An oxygen-sulfur potential diagram was constructed in relation to matte grade, and it was found that the ratio of (pO<SUB>2</SUB>⁄pS<SUB>2</SUB>) was constant against pSO<SUB>2</SUB> when the matte grade was specified. The solubility of sulfur in the slag and that of oxygen in the matte decreased with increasing matte grade and the SO2 partial pressure gave no significant effect on these solubilities within the investigated pSO<SUB>2</SUB> range. On the other hand, the solubility of nickel in the slag increased with increasing pSO<SUB>2</SUB> at a given matte grade and this behavior was analyzed thermodynamically based on a concept of oxidic and sulfidic dissolution of components in the slag.
収録刊行物
-
- Materials Transactions, JIM
-
Materials Transactions, JIM 39 (6), 652-657, 1998
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204248398592
-
- NII論文ID
- 130003557051
- 10003802924
-
- NII書誌ID
- AA10699969
-
- COI
- 1:CAS:528:DyaK1cXkvF2hsbw%3D
-
- ISSN
- 2432471X
- 09161821
-
- NDL書誌ID
- 4505431
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可