Corrosion Resistance of Alumina-Chromia Ceramic Materials Against Molten Slag
-
- Hirata Takehiko
- Advanced Technology Research Center, Mitsubishi Heavy Industries, Ltd.
-
- Morimoto Tatsuo
- Advanced Technology Research Center, Mitsubishi Heavy Industries, Ltd.
-
- Deguchi Akio
- Yokohama Research and Development Center, Mitsubishi Heavy Industries, Ltd.
-
- Uchida Nozomu
- Nagaoka University of Technology
この論文をさがす
抄録
Improvement of the corrosion resistance of refractories is required critically, since Al2O3 based conventional refractories used for incineration at the power generation plants are seriously corroded by the molten oxide mixture. In this study, the effect of the addition of Cr2O3 to Al2O3 on the corrosion resistance, and the corrosion behavior of Cr2O3–Al2O3 system are investigated in the molten oxide. Cr2O3–Al2O3 ceramic materials with TiO2 as a sintering additive were used for the corrosion tests. Specimens were soaked into the SiO2–CaO–Al2O3 based molten oxide and rotated. The corrosion rate of the material is controlled by the diffusion of components of Cr2O3–Al2O3 through the boundary layer. The corrosion resistance was improved by addition of Cr2O3. The largest improvement was achieved when the addition of Cr2O3 was 81.6 mol%. It can be explained by the difference of diffusion rate of Cr3+ and Al3+.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (10), 2561-2567, 2002
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204248477568
-
- NII論文ID
- 130004451686
- 10012327326
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD38XptVyks7s%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6341437
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可