Biomechanical Evaluation of Amorphous Calcium Phosphate Coated TNTZ Implants Prepared Using a Radiofrequency Magnetron Sputtering System
-
- Shiraishi Naru
- Research Unit for Interface Oral Health Science, Graduate School of Dentistry, Tohoku University
-
- Tu Rong
- Institute for Materials Research, Tohoku University
-
- Uzuka Risa
- Division of Advanced Prosthetic Dentistry, Graduate School of Dentistry, Tohoku University
-
- Anada Takahisa
- Division of Craniofacial Function Engineering, Graduate School of Dentistry, Tohoku University
-
- Narushima Takayuki
- Department of Materials Processing, Graduate School of Engineering, Tohoku University
-
- Goto Takashi
- Institute for Materials Research, Tohoku University
-
- Niinomi Mitsuo
- Institute for Materials Research, Tohoku University
-
- Sasaki Keiichi
- Division of Advanced Prosthetic Dentistry, Graduate School of Dentistry, Tohoku University
-
- Suzuki Osamu
- Division of Craniofacial Function Engineering, Graduate School of Dentistry, Tohoku University
この論文をさがす
抄録
Ti–29Nb–13Ta–4.6Zr alloy (TNTZ), a new β-type Ti alloy, has excellent advantages as a biomaterial, such as low Young’s modulus and cytotoxicity, and the absence of allergens. However, it is unclear whether TNTZ can achieve sufficient osseointegration for it to be used as a dental implant. The effectiveness of surface modification of TNTZ implants by radiofrequency (RF) magnetron sputtering is also unclear. We investigated the biomechanical behaviors of TNTZ implants in vivo, using cylindrical implants of four types: pure Ti, TNTZ, and pure Ti and TNTZ coated with amorphous calcium phosphate (ACP). The implants were inserted in rat femurs, and the femurs were subjected to biomechanical analyses after various time intervals. The results suggest that TNTZ implants can achieve osseointegration similar to that of pure Ti, and that surface modification with ACP by RF magnetron sputtering improves osseointegration, especially in the later stages of healing.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 53 (7), 1343-1348, 2012
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204249016960
-
- NII論文ID
- 120006846725
- 10030792226
- 130004824926
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BC38Xhtlantr3E
-
- ISSN
- 13475320
- 13459678
-
- HANDLE
- 10097/00127759
-
- NDL書誌ID
- 023781892
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可