Deformation and Recrystallization in Lightly-Rolled Aluminum Single Crystals of Cube Orientation

DOI Web Site Web Site 被引用文献2件 参考文献34件
  • Okada Tatsuya
    Department of Mechanical Engineering, Faculty of Engineering, Tokushima University
  • Soga Akiyo
    Department of Mechanical Engineering, Faculty of Engineering, Tokushima University
  • Tamura Kouji
    Department of Mechanical Engineering, Faculty of Engineering, Tokushima University
  • Tagami Minoru
    Department of Mechanical Engineering, Faculty of Engineering, Tokushima University
  • Inoko Fukuji
    Emeritus Professor, Tokushima University

この論文をさがす

説明

Deformation and recrystallization of 17%- and 34%-rolled aluminum single crystals of cube orientation were studied. Most slip bands observed in the TD surface were straight and the occurrences of cross-slip were small. There was a relatively large orientation variation in the TD surface and the deviation from the initial orientation reached 10° in the 34%-rolled sample. After annealing, recrystallized grains were formed both at the rolled surfaces and around the middle of the thickness of the sample. Two thirds of the recrystallized grains had ⟨111⟩-rotation relationships with the deformed matrix. Although all ⟨111⟩-rotation relationships were found, their occurrences were not the same. Above results are compared with those obtained in tensile-deformed aluminum single crystals with the same initial orientation.