Laser Forming of Zr-Based Coatings on AZ91D Magnesium Alloy Substrates for Wear and Corrosion Resistance Improvement
-
- Yue T. M.
- The Advanced Manufacturing Technology Research Centre, Department of Industrial and Systems Engineering, The Hong Kong Polytechnic University
-
- Huang K. J.
- The Advanced Manufacturing Technology Research Centre, Department of Industrial and Systems Engineering, The Hong Kong Polytechnic University
この論文をさがす
抄録
To improve the wear and corrosion resistance of AZ91D magnesium alloy, Zr-based coatings were fabricated on the alloy substrate using laser forming. They were prepared from (i) Zr+Mg powders (5:1 mass%), and (ii) an undercoating of Zr+Mg powders (5:1 mass%) with a top layer of Zr powder. The Zr+Mg powder coating was found to consist primarily of Zr particles with some Zr-based intermetallic compounds in a Mg-Al matrix; while that with an extra top coating of Zr powder had an outer layer composed of Zr oxides and Zr aluminides. With regard to wear and corrosion resistance, the highest improvement was obtained for the specimen that was clad with a top layer of Zr powder. Compared to the AZ91D specimen without a laser formed coating, a fivefold decrease in weight loss and around three orders of magnitude decrease in corrosion current density respectively were obtained.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 52 (4), 810-813, 2011
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204249270784
-
- NII論文ID
- 10028175693
- 130004454705
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BC3MXovVyqurc%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 11058417
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可