Effect of Environmentally Friendly Anodization on the Mechanical Properties and Microstructure of AZ91D Magnesium Alloy
-
- Saijo Atsushi
- Hori Metal Finishing Industry, Co. Ltd.
-
- Murakami Koji
- Industrial Technology Research Institute of Okayama Prefectural Government
-
- Hino Makoto
- Industrial Technology Research Institute of Okayama Prefectural Government
-
- Kanadani Teruto
- Faculty of Engineering, Okayama University of Science
この論文をさがす
抄録
Die-cast plates of ASTM (American Society for Testing and Materials) AZ91D magnesium alloy were anodized by DC or AC electrolysis in a solution of phosphate and ammonium salt in which the anodized layer is formed by local discharge, followed by rapid solidification. Salt spray tests of the anodized specimens showed that AC electrolysis increases corrosion resistance and the anodized layers become denser compared with that for DC electrolysis. Tensile strength, elongation, and hardness were also improved by anodization, but higher anodizing bias and the resulting heating caused grain coarsening and a decrease in these properties. For the specimens that displayed remarkable improvement in mechanical properties, a decrease in network precipitates of the β phase was observed. Improvement of mechanical properties is considered to be due to the fine precipitation of β inside the grains of the α phase at moderate temperature.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 49 (5), 903-908, 2008
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204249361664
-
- NII論文ID
- 10021146229
- 130004454004
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 9480118
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可