Formation of Nanotwins in Cold-Rolled Cu-Zn Alloy by Electric Current Pulses

DOI Web Site Web Site 被引用文献1件 参考文献32件
  • Dai Wenbin
    School of Materials and Metallurgy, Northeastern University
  • Wang Xinli
    School of Materials and Metallurgy, Northeastern University
  • Zhao Lin
    China First Heavy Industries
  • Yu Jingkun
    School of Materials and Metallurgy, Northeastern University

この論文をさがす

説明

A significant number of nanotwins was fabricated in a cold-rolled Cu-Zn alloy after an electric current pulse (ECP) treatment in this study. Results showed that the formation of nanotwins was related not only to the α to β phase transformation, but also to the effect of the enhanced directional nucleation along the current direction during the heating caused by the ECP treatment. A theoretical analysis revealed that the nucleation rate of the higher conductivity phase (β phase) was significantly accelerated by the application of an electric current, which provided more nucleation places for the α phase during the subsequent rapid cooling process. Especially, during the cooling process, nanotwins with {111} twin planes in the α phase would be formed due to the stronger internal stress induced by the rapid cooling rate after the ECP treatment.

収録刊行物

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 52 (11), 2022-2026, 2011

    公益社団法人 日本金属学会

被引用文献 (1)*注記

もっと見る

参考文献 (32)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ