Effects of Ta on Microstructure and Mechanical Property of Ti-Zr-Cu-Pd-Ta Alloys
-
- Qin F. X.
- Institute for Materials Research, Tohoku University
-
- Wang X. M.
- Institute for Materials Research, Tohoku University
-
- Inoue A.
- Institute for Materials Research, Tohoku University
この論文をさがす
抄録
The effects of Ta on microstructure and mechanical property of Ti-Zr-Cu-Pd-Ta alloys without toxic element were investigated in this paper. The results revealed that with increasing Ta content, the glass-forming ability of examined alloys decreased. Nano-crystalline composites were obtained with 1% and 3% Ta addition. Higher strength and distinct plastic deformation comparing with Ti-Zr-Cu-Pd base alloy were achieved in 1% Ta-containing alloys due to the nano-particles existing in the glassy matrix which inhibit the deformation of shear bands. Dendrite enriched with Ta was also observed in the 5% Ta-containing alloy by SEM. No plastic deformation was observed for 3% and 5% Ta-containing alloys with the high volume fractions of crystallization over 50%.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 48 (9), 2390-2394, 2007
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204249569664
-
- NII論文ID
- 10019853577
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 8885158
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可