Sintering Behavior of Tungsten Heavy Alloy Products Made by Plasma Spray Forming
-
- Wang Yueming
- State Key Laboratory of Powder Metallurgy, Central South University
-
- Xiong Xiang
- State Key Laboratory of Powder Metallurgy, Central South University
-
- Xie Lu
- State Key Laboratory of Powder Metallurgy, Central South University
-
- Xu Xuan
- State Key Laboratory of Powder Metallurgy, Central South University
-
- Min Xiaobing
- Hunan Research Institute of Metallurgy and Materials
-
- Zheng Feng
- School of Materials Science and Engineering, Central South University
この論文をさがす
抄録
Refractory metallic thin-walled products of 95W–3.5Ni–1.5Fe (in mass%) were fabricated by plasma spray forming (PSF) in argon atmosphere at 1.01×105 Pa followed by high temperature sintering (1200, 1300, 1400 and 1465°C). Scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDS), Archimedes method, differential scanning calorimetry (DSC) and X-ray diffractometer (XRD) have been employed to study microstructure, solubilities, density, solidus and liquidus temperatures and phases of the parts. Lamellar structure consisting of vertical columnar grains and fine particles was found in PSF deposits. Supersaturated solid solutions were formed in the deposits with the relative density of 88±2%. Solidus and liquidus temperatures of γ phase were measured to be 1392 and 1412±5°C, respectively. Initial lamellar structure was remained in the tested samples after sintering at lower temperatures (1200°C/90 min, 1300°C/90 min and 1400°C/15, 90 min) and turned into granular structure at 1465°C/5, 15, 30, 90 min. In addition, the relative densities of deposits, after sintering at 1200, 1300, 1400 and 1465°C for 90 min, were increased from 88 to 90, 92, 94 and 98±2%, respectively. A five-stage sintering mechanism proposed by us previously has been re-validated and double checked by experimental results.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 52 (4), 759-767, 2011
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204249588864
-
- NII論文ID
- 10028175520
- 130004454699
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BC3MXovVyqur8%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 11058372
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可