Alloying Behavior of Ni<SUB>3</SUB>M-Type Compounds with D0<SUB>a</SUB> Structure

DOI Web Site Web Site 2 Citations 87 References
  • Sugimura H.
    Department of Materials Science, Osaka Prefecture University
  • Kaneno Y.
    Department of Materials Science, Osaka Prefecture University
  • Takasugi T.
    Department of Materials Science, Osaka Prefecture University

Bibliographic Information

Other Title
  • Alloying behavior of Ni3M-type compounds with D0a structure

Search this article

Abstract

The atom substitution preference of ternary additions in Ni3M-type GCP (geometrically close-packed) compounds with D0a structure was determined from the direction of single-phase region of the GCP phase on the reported ternary phase diagrams. In Ni3Nb, Co and Cu preferred the substitution for Ni-site, Hf, Ta, Ti, V and W the substitution for Nb-site, and Fe the substitution for both sites. In Ni3Ta, Co, Cu, Fe, Ir, Mn and Re preferred the substitution for Ni-site, Mo and Nb the substitution for Ta-site, and Al and Cr the substitution for both sites. In Ni3Mo, Pd and W preferred the substitution for Ni-site, and Al, Nb, Ta, Ti and Zr the substitution for Mo-site. The thermodynamic model, which was based on the change in heat of formation of the host compound by a small addition of ternary solute, was applied to predict the atom substitution preference of ternary additions. The heat of compound formation used in the thermodynamic calculation was derived from Miedema’s formula. Good agreement was obtained between the thermodynamic model and the result of the literature search. For Ni3Mo, with a small negative heat of formation, a weak binding force between the constituent elements is often enhanced by the addition of the ternary elements that substitute for Mo-site.

Journal

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 52 (4), 663-671, 2011

    The Japan Institute of Metals and Materials

Citations (2)*help

See more

References(87)*help

See more

Related Projects

See more

Keywords

Details 詳細情報について

Report a problem

Back to top